Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate + ABS
Product No: CYCOLOY FR Resin CM6210
Product Quantity: 25KG / BAG
Product Features: Bromine Free,Chlorine Free,Flame Retardant,High Stiffness
CYCOLOY? FR Resin CM6210
Additive |
|
Features |
|
Uses |
|
Processing Method |
|
Also Available In |
|
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | |||
-- | 1.28 | ASTM D792 | |
-- | 1.27 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 0.549 | in3/10min | ISO 1133 |
Molding Shrinkage - Flow (0.126 in) | 4.0E-3 to 6.0E-3 | in/in | Internal Method |
Water Absorption | ISO 62 | ||
Saturation, 73°F | 0.30 | % | |
Equilibrium, 73°F, 50% RH | 0.10 | % | |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 98 | ISO 2039-2 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 518000 | psi | ASTM D638 |
-- | 531000 | psi | ISO 527-2/1 |
Tensile Strength | |||
Yield 4 | 9280 | psi | ASTM D638 |
Yield | 8560 | psi | ISO 527-2/5 |
Yield | 9140 | psi | ISO 527-2/50 |
Break 4 | 7250 | psi | ASTM D638 |
Break | 9430 | psi | ISO 527-2/5 |
Break | 7250 | psi | ISO 527-2/50 |
Tensile Elongation | |||
Yield 4 | 4.9 | % | ASTM D638 |
Yield | 3.6 | % | ISO 527-2/5 |
Yield | 3.5 | % | ISO 527-2/50 |
Break 4 | 80 | % | ASTM D638 |
Break | 100 | % | ISO 527-2/5 |
Break | 97 | % | ISO 527-2/50 |
Flexural Modulus | |||
1.97 in Span 5 | 508000 | psi | ASTM D790 |
-- 6 | 516000 | psi | ISO 178 |
Flexural Stress | |||
-- 6, 7 | 15400 | psi | ISO 178 |
Yield, 1.97 in Span 5 | 16000 | psi | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
-22°F | 4.8 | ft·lb/in2 | |
73°F | 21 | ft·lb/in2 | |
Notched Izod Impact | |||
-22°F | 1.7 | ft·lb/in | ASTM D256 |
73°F | 9.4 | ft·lb/in | ASTM D256 |
-22°F 9 | 4.8 | ft·lb/in2 | ISO 180/1A |
73°F 9 | 21 | ft·lb/in2 | ISO 180/1A |
Instrumented Dart Impact (73°F, Total Energy) | 398 | in·lb | ASTM D3763 |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
66 psi, Unannealed, 0.157 in, 3.94 in Span 10 | 210 | °F | ISO 75-2/Be |
264 psi, Unannealed, 0.126 in | 194 | °F | ASTM D648 |
264 psi, Unannealed, 0.157 in, 3.94 in Span 10 | 192 | °F | ISO 75-2/Ae |
Vicat Softening Temperature | |||
-- | 223 | °F | ASTM D1525 11 |
-- | 234 | °F | ISO 306/B50 |
-- | 237 | °F | ISO 306/B120 |
Ball Pressure Test | IEC 60695-10-2 | ||
163 to 171°F | Pass | ||
203°F 12 | Pass | ||
CLTE | |||
Flow : -40 to 104°F | 3.2E-5 | in/in/°F | ASTM E831 |
Flow : -40 to 104°F | 2.9E-5 | in/in/°F | ISO 11359-2 |
Flow : 73 to 140°F | 2.9E-5 | in/in/°F | ISO 11359-2 |
Transverse : -40 to 104°F | 3.9E-5 | in/in/°F | ASTM E831 |
Transverse : -40°F | 3.3E-5 | in/in/°F | ISO 11359-2 |
Transverse : 73 to 140°F | 3.3E-5 | in/in/°F | ISO 11359-2 |
Thermal Conductivity | 2.1 | Btu·in/hr/ft2/°F | ISO 8302 |
RTI Elec | 140 | °F | UL 746 |
RTI Imp | 140 | °F | UL 746 |
RTI Str | 140 | °F | UL 746 |
Electrical | Nominal Value | Unit | Test Method |
Electric Strength | IEC 60243-1 | ||
0.0315 in, in Oil | 970 | V/mil | |
0.0630 in, in Oil | 660 | V/mil | |
0.126 in, in Oil | 430 | V/mil | |
Relative Permittivity | IEC 60250 | ||
50 Hz | 2.90 | ||
60 Hz | 2.90 | ||
1 MHz | 2.80 | ||
Dissipation Factor | IEC 60250 | ||
50 Hz | 3.0E-3 | ||
60 Hz | 3.0E-3 | ||
1 MHz | 4.0E-3 | ||
Comparative Tracking Index | 250 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating (0.06 in) | V-0 | UL 94 |
Extrusion Notes | |||
Sheet Extrusion Parameters
|
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields