Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate + ABS
Product No: CYCOLOY FR Resin CX7240U
Product Quantity: 25KG / BAG
Product Features: Bromine Free，Chlorine Free，Flame Retardant，Good Flow，Good Impact Resistance
CYCOLOY? FR Resin CX7240U
Additive |
|
Features |
|
Uses |
|
Processing Method |
|
Also Available In |
|
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | |||
-- | 1.19 | ASTM D792 | |
-- | 1.20 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 0.915 | in3/10min | ISO 1133 |
Molding Shrinkage - Flow (0.126 in) | 4.0E-3 to 6.0E-3 | in/in | Internal Method |
Water Absorption | ISO 62 | ||
Saturation, 73°F | 0.20 | % | |
Equilibrium, 73°F, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 428000 | psi | ASTM D638 |
-- | 367000 | psi | ISO 527-2/1 |
Tensile Strength | |||
Yield 4 | 9430 | psi | ASTM D638 |
Yield | 9430 | psi | ISO 527-2/50 |
Break 4 | 8410 | psi | ASTM D638 |
Break | 7250 | psi | ISO 527-2/50 |
Tensile Elongation | |||
Yield 4 | 4.1 | % | ASTM D638 |
Yield | 4.0 | % | ISO 527-2/50 |
Break 4 | 100 | % | ASTM D638 |
Break | 90 | % | ISO 527-2/50 |
Flexural Modulus | |||
1.97 in Span 5 | 399000 | psi | ASTM D790 |
-- 6 | 363000 | psi | ISO 178 |
Flexural Stress | |||
-- 6, 7 | 13900 | psi | ISO 178 |
Yield, 1.97 in Span 5 | 15100 | psi | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
-22°F | 4.8 | ft·lb/in2 | |
73°F | 9.5 | ft·lb/in2 | |
Notched Izod Impact | |||
-22°F | 1.9 | ft·lb/in | ASTM D256 |
73°F | 9.4 | ft·lb/in | ASTM D256 |
-22°F 9 | 4.8 | ft·lb/in2 | ISO 180/1A |
73°F 9 | 9.5 | ft·lb/in2 | ISO 180/1A |
Instrumented Dart Impact (73°F, Total Energy) | 575 | in·lb | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
66 psi, Unannealed, 0.126 in | 212 | °F | ASTM D648 |
264 psi, Unannealed, 0.126 in | 192 | °F | ASTM D648 |
264 psi, Unannealed, 0.252 in | 210 | °F | ASTM D648 |
264 psi, Unannealed, 0.157 in, 2.52 in Span 10 | 199 | °F | ISO 75-2/Af |
Vicat Softening Temperature | |||
-- | 223 | °F | ASTM D1525 11 |
-- | 230 | °F | ISO 306/B50 |
-- | 235 | °F | ISO 306/B120 |
Ball Pressure Test (163 to 171°F) | Pass | IEC 60695-10-2 | |
CLTE | |||
Flow : -40 to 104°F | 3.5E-5 | in/in/°F | ASTM E831 |
Flow : -40 to 104°F | 3.4E-5 | in/in/°F | ISO 11359-2 |
Transverse : -40 to 104°F | 3.0E-5 | in/in/°F | ASTM E831 |
Transverse : -40°F | 3.0E-5 | in/in/°F | ISO 11359-2 |
RTI Elec | 194 | °F | UL 746 |
RTI Imp | 194 | °F | UL 746 |
RTI Str | 194 | °F | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
High Amp Arc Ignition (HAI) 12 | PLC 0 | UL 746 | |
Hot-wire Ignition (HWI) | PLC 3 | UL 746 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
0.016 in | V-2 | ||
0.024 in | V-1 | ||
0.030 in | V-0 | ||
0.06 in | 5VB | ||
0.12 in | 5VA | ||
Glow Wire Flammability Index (0.030 in) | 1760 | °F | IEC 60695-2-12 |
Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
0.04 in | 1520 | °F | |
0.12 in | 1470 | °F |
| Injection | Nominal Value | Unit | |
Drying Temperature | 194 | °F | |
Drying Time | 4.0 | hr | |
Suggested Max Moisture | 0.040 | % | |
Suggested Shot Size | 40 to 80 | % | |
Hopper Temperature | 140 to 176 | °F | |
Rear Temperature | 500 to 572 | °F | |
Middle Temperature | 500 to 572 | °F | |
Front Temperature | 509 to 572 | °F | |
Nozzle Temperature | 509 to 572 | °F | |
Processing (Melt) Temp | 518 to 572 | °F | |
Mold Temperature | 140 to 194 | °F | |
Back Pressure | 43.5 to 102 | psi | |
Screw Speed | 40 to 70 | rpm | |
Vent Depth | 1.5E-3 to 3.0E-3 | in |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields