Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate + ABS
Product No: CYCOLOY Resin C1200HF
Product Quantity: 25KG / BAG
Product Features: Ductile，Good Flow，Good Impact Resistance，High Heat Resistance
CYCOLOY? Resin C1200HF
Features | DuctileGood FlowGood Impact ResistanceHigh Heat Resistance |
Processing Method |
|
Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.15 | ASTM D792 | |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 1.46 | in3/10min | ISO 1133 |
Molding Shrinkage - Flow (0.126 in) | 5.0E-3 to 7.0E-3 | in/in | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 330000 | psi | ASTM D638 |
-- | 344000 | psi | ISO 527-2/1 |
Tensile Strength | |||
Yield 4 | 8300 | psi | ASTM D638 |
Yield | 7980 | psi | ISO 527-2/50 |
Tensile Elongation | |||
Yield 4 | 5.0 | % | ASTM D638 |
Yield | 4.8 | % | ISO 527-2/50 |
Break 4 | 150 | % | ASTM D638 |
Break | 110 | % | ISO 527-2/50 |
Flexural Modulus | |||
1.97 in Span 5 | 340000 | psi | ASTM D790 |
-- | 327000 | psi | ISO 178 |
Flexural Stress | |||
-- | 12500 | psi | ISO 178 |
Yield, 1.97 in Span 5 | 12800 | psi | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | |||
-22°F | 9.0 | ft·lb/in | ASTM D256 |
73°F | 11 | ft·lb/in | ASTM D256 |
-22°F 6 | 16 | ft·lb/in2 | ISO 180/1A |
73°F 6 | 23 | ft·lb/in2 | ISO 180/1A |
Instrumented Dart Impact | ASTM D3763 | ||
-22°F, Total Energy | 480 | in·lb | |
73°F, Total Energy | 480 | in·lb |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
66 psi, Unannealed, 0.126 in | 265 | °F | ASTM D648 |
66 psi, Unannealed, 2.52 in Span 7 | 266 | °F | ISO 75-2/Bf |
264 psi, Unannealed, 0.126 in | 235 | °F | ASTM D648 |
264 psi, Unannealed, 2.52 in Span 7 | 230 | °F | ISO 75-2/Af |
Vicat Softening Temperature | 266 | °F | ISO 306/B50 |
CLTE - Flow (-40 to 104°F) | 4.0E-5 | in/in/°F | ASTM E831 |
RTI Elec | 221 | °F | UL 746 |
RTI Imp | 176 | °F | UL 746 |
RTI Str | 221 | °F | UL 746 |
| Electrical | Nominal Value | Test Method | |
Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
Hot-wire Ignition (HWI) | PLC 3 | UL 746 | |
| Flammability | Nominal Value | Test Method | |
Flame Rating (0.05 in) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
Drying Temperature | 212 to 230 | °F | |
Drying Time | 3.0 to 4.0 | hr | |
Drying Time, Maximum | 8.0 | hr | |
Suggested Max Moisture | 0.020 | % | |
Suggested Shot Size | 30 to 80 | % | |
Hopper Temperature | 140 to 176 | °F | |
Rear Temperature | 482 to 554 | °F | |
Middle Temperature | 491 to 563 | °F | |
Front Temperature | 500 to 572 | °F | |
Nozzle Temperature | 527 to 572 | °F | |
Processing (Melt) Temp | 527 to 572 | °F | |
Mold Temperature | 140 to 194 | °F | |
Back Pressure | 43.5 to 102 | psi | |
Screw Speed | 40 to 70 | rpm | |
Vent Depth | 1.5E-3 to 3.0E-3 | in |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields