Manufacturer: DUPONT
Produced At: Import/ China
Product Category: PBT
Product No: Crastin FGS600F40 NC010
Product Quantity: 25KG / BAG
Product Features: Food Contact Acceptable,Low Viscosity
Crastin? FGS600F40 NC010
Features |
|
Uses |
|
RoHS Compliance |
|
Forms |
|
Processing Method |
|
Multi-Point Data |
|
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
|
Physical | Nominal Value | Unit | Test Method |
Density | 1.31 | g/cm3 | ISO 1183 |
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 2.01 | in3/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.6 | % | |
Flow | 1.6 | % | |
Water Absorption | ISO 62 | ||
Saturation, 73°F, 0.0787 in | 0.40 | % | |
Equilibrium, 73°F, 0.0787 in, 50% RH | 0.20 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 348000 | psi | ISO 527-2 |
Tensile Stress (Yield) | 7980 | psi | ISO 527-2 |
Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
Nominal Tensile Strain at Break | 30 | % | ISO 527-2 |
Tensile Creep Modulus | ISO 899-1 | ||
1 hr | 377000 | psi | |
1000 hr | 261000 | psi | |
Poisson's Ratio | 0.38 | ISO 527 | |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-22°F | 1.9 | ft·lb/in2 | |
73°F | 1.9 | ft·lb/in2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-22°F | No Break | ||
73°F | No Break |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
66 psi, Unannealed | 239 | °F | ISO 75-2/B |
66 psi, Annealed | 356 | °F | ISO 75-2/B |
264 psi, Unannealed | 122 | °F | ISO 75-2/A |
264 psi, Annealed | 140 | °F | ISO 75-2/A |
Glass Transition Temperature 3 | 131 | °F | ISO 11357-2 |
Vicat Softening Temperature | 347 | °F | ISO 306/B50 |
Melting Temperature 3 | 433 | °F | ISO 11357-3 |
CLTE | ISO 11359-2 | ||
Flow | 6.1E-5 | in/in/°F | |
Transverse | 6.7E-5 | in/in/°F |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | 660 | V/mil | IEC 60243-1 |
Dissipation Factor | IEC 60250 | ||
100 Hz | 2.0E-3 | ||
1 MHz | 0.020 | ||
Comparative Tracking Index | 600 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Burning Rate 4 (0.0394 in) | 1.1 | in/min | ISO 3795 |
Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
0.06 in | HB | ||
0.12 in | HB | ||
Oxygen Index | 22 | % | ISO 4589-2 |
FMVSS Flammability | B | FMVSS 302 | |
Fogging | ISO 6452 | ||
F-value (refraction) | 95 | % | |
G-value (condensate) | 2.0E-4 | g |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Density | 1.11 | g/cm3 | |
Ejection Temperature | 338 | °F | |
Specific Heat Capacity of Melt | 0.504 | Btu/lb/°F | |
Thermal Conductivity of Melt | 1.5 | Btu·in/hr/ft2/°F | |
Additional Information | Nominal Value | Unit | Test Method |
Odor | 3.00 | VDA 270 |
Injection | Nominal Value | Unit | |
Drying Temperature | 248 | °F | |
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
Suggested Max Moisture | 0.040 | % | |
Processing (Melt) Temp | 464 to 500 | °F | |
Melt Temperature, Optimum | 482 | °F | |
Mold Temperature | 86 to 266 | °F | |
Mold Temperature, Optimum | 176 | °F | |
Holding Pressure | 8700 | psi | |
Back Pressure | As low as possible | ||
Drying Recommended | yes | ||
Hold Pressure Time | 4.00 | s/mm |