Manufacturer: RTP Company
Produced At: Import / China
Product Category: Polyetheretherketone(PEEK)
Product No: RTP 2281
Product Quantity: 25KG / BAG
Product Features: Electrically Conductive
RTP 2281
Filler / Reinforcement |
|
Features |
|
RoHS Compliance |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.33 | ASTM D792 | |
Molding Shrinkage - Flow (0.125 in) | 1.0E-3 to 2.0E-3 | in/in | ASTM D955 |
Water Absorption (24 hr, 73°F) | 0.15 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 1.70E+6 | psi | ASTM D638 |
Tensile Strength | 27000 | psi | ASTM D638 |
Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
Flexural Modulus | 1.40E+6 | psi | ASTM D790 |
Flexural Strength | 39000 | psi | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (0.125 in) | 0.70 | ft·lb/in | ASTM D256 |
Unnotched Izod Impact (0.125 in) | 8.0 | ft·lb/in | ASTM D4812 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
66 psi, Unannealed | 550 | °F | |
264 psi, Unannealed | 550 | °F |
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating (0.06 in) | V-0 | UL 94 |
Additional Information | |||
Tensile Elongation, ASTM D638: 2-3% Volume Resistivity, ASTM D257: 1E4-1E6 ohm-cm |
Injection | Nominal Value | Unit | |
Drying Temperature | 300 | °F | |
Drying Time | 3.0 | hr | |
Suggested Max Moisture | 0.10 | % | |
Suggested Max Regrind | 20 | % | |
Rear Temperature | 675 to 750 | °F | |
Middle Temperature | 675 to 750 | °F | |
Front Temperature | 675 to 750 | °F | |
Mold Temperature | 300 to 400 | °F | |
Injection Pressure | 10000 to 15000 | psi | |
Back Pressure | 50.0 to 100 | psi | |
Clamp Tonnage | 5.0 to 8.0 | tons/in2 |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields