Manufacturer: DSM
Produced At: Europe / China
Product Category: Polyamide 410(PA410)
Product No: EcoPaXX Q-KG5
Product Quantity: 25KG / BAG
Product Features: Additive Mold Release
EcoPaXX? Q-KG5
Contains release agent
Filler / Reinforcement |
|
Additive |
|
Processing Method |
|
Resin ID (ISO 1043) |
|
Physical | Nominal Value | Unit | Test Method |
Density | 1.28 | g/cm3 | ISO 1183 |
Biobased Content | 70 | % | ASTM D6866B |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 1.16E+6 | psi | ISO 527-2 |
Tensile Stress (Break) | 23200 | psi | ISO 527-2 |
Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
Flexural Modulus | 1.09E+6 | psi | ISO 178 |
Flexural Stress | 36300 | psi | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-22°F | 3.6 | ft·lb/in2 | |
73°F | 4.0 | ft·lb/in2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-22°F | 26 | ft·lb/in2 | |
73°F | 31 | ft·lb/in2 |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
66 psi, Unannealed | 464 | °F | ISO 75-2/B |
264 psi, Unannealed | 428 | °F | ISO 75-2/A |
Melting Temperature 2 | 482 | °F | ISO 11357-3 |
Injection | Nominal Value | Unit | |
Drying Temperature | 176 | °F | |
Drying Time | 2.0 to 4.0 | hr | |
Rear Temperature | 482 to 518 | °F | |
Middle Temperature | 500 to 536 | °F | |
Front Temperature | 518 to 554 | °F | |
Nozzle Temperature | 518 to 572 | °F | |
Processing (Melt) Temp | 527 to 590 | °F | |
Mold Temperature | 176 to 284 | °F | |
Injection Rate | Moderate-Fast | ||
Back Pressure | 435 to 1450 | psi | |
Screw Compression Ratio | 2.5:1.0 |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields