Manufacturer: BASF
Produced At: Europe / China
Product Category: PBT + PET
Product No: Ultradur B4040 G6
Product Quantity: 25KG / BAG
Product Features: Outstanding Surface Finish
Ultradur? B 4040 G6
Filler / Reinforcement |
|
Features |
|
Uses | Appliance Components、Automotive Applications、Handles、Industrial Parts |
Agency Ratings |
|
RoHS Compliance |
|
Appearance | Black、Colors Available |
Forms |
|
Processing Method |
|
Multi-Point Data | Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
Density | 1.55 | g/cm3 | ISO 1183 |
Apparent (Bulk) Density | 0.70 to 0.80 | g/cm3 | |
Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 0.915 | in3/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 0.90 | % | |
Flow | 0.30 | % | |
Water Absorption | ISO 62 | ||
Saturation, 73°F | 0.40 | % | |
Equilibrium, 73°F, 50% RH | 0.20 | % | |
Viscosity Number 3 | 105 | cm3/g | ISO 307 |
Mold Shrinkage 4 | |||
free, longitudinal | 0.18 | % | |
free, transverse | 0.99 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 1.52E+6 | psi | ISO 527-2 |
Tensile Stress (Break) | 21000 | psi | ISO 527-2 |
Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (73°F) | 3.8 | ft·lb/in2 | ISO 179/1eA |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-22°F | 26 | ft·lb/in2 | |
73°F | 29 | ft·lb/in2 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
66 psi, Unannealed | 428 | °F | ISO 75-2/B |
264 psi, Unannealed | 392 | °F | ISO 75-2/A |
Melting Temperature | 433 | °F | ISO 11357-3 |
CLTE - Flow (73 to 176°F) | 1.1E-5 to 1.7E-5 | in/in/°F | ISO 11359-2 |
Specific Heat | 0.251 | Btu/lb/°F | |
Maximum Service Temperature - short cycle operation | 410 | °F | |
Temperature Index - at 50% loss of tensile strength | IEC 60216 | ||
-- 5 | 284 | °F | |
-- 6 | 320 | °F |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
Relative Permittivity | IEC 60250 | ||
100 Hz | 4.00 | ||
1 MHz | 3.80 | ||
Dissipation Factor | IEC 60250 | ||
100 Hz | 1.6E-3 | ||
1 MHz | 0.017 | ||
Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
Flammability Classification | IEC 60695-11-10, -20 | ||
0.030 in | HB | ||
0.06 in | HB |
| Injection | Nominal Value | Unit | |
Drying Temperature | 176 to 248 | °F | |
Drying Time | 4.0 | hr | |
Suggested Max Moisture | 0.040 | % | |
Hopper Temperature | 176 | °F | |
Rear Temperature | 500 | °F | |
Middle Temperature | 509 | °F | |
Front Temperature | 518 | °F | |
Nozzle Temperature | 518 | °F | |
Processing (Melt) Temp | 482 to 536 | °F | |
Mold Temperature | 140 to 212 | °F | |
Screw Speed | < 591 | in/min |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields