Manufacturer: TOYOBO
Produced At: Japan / China
Product Category: TPEE
Product No: PELPRENE P70B
Product Quantity: 25KG / BAG
Product Features: Flame Rated/Chemical Resistant/Copolymer/Good Processability/Heat Resistant
PELPRENE? P70B
Features | Flame Rated/Chemical Resistant/Copolymer/Good Processability/Heat Resistant |
Uses |
|
Forms |
|
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.17 | ASTM D792 | |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow (0.0787 in) | 0.010 | in/in | ASTM D955 |
Water Absorption (Equilibrium, 73°F, 65% RH) | 0.43 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
Durometer Hardness (Shore D) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength (Yield) | 4350 | psi | ASTM D638 |
Tensile Elongation (Break) | 550 | % | ASTM D638 |
Flexural Modulus | 15700 | psi | ASTM D790 |
Compressive Modulus | 1330 | psi | ASTM D695 |
Taber Abrasion Resistance (1000 Cycles) | 15.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
Tensile Stress (50% Strain) | 1570 | psi | ASTM D412 |
Tear Strength | 697 | lbf/in | ASTM D624 |
Compression Set | 55 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (264 psi, Unannealed) | 165 | °F | ASTM D648 |
Brittleness Temperature | -85.0 | °F | ASTM D746 |
Vicat Softening Temperature | 338 | °F | ASTM D1525 |
Melting Temperature | 392 | °F | DSC |
CLTE - Flow | 8.9E-5 | in/in/°F | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 6.0E+13 | ohms·cm | ASTM D257 |
Dielectric Strength | 640 | V/mil | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | HB | UL 94 |
| Additional Information | |||
Hardness, JIS k6301, A scale: 96 10% Compression Modulus, ASTM D695: 9.2 MPa Resilience, JIS K6301: 71 % Brittle Point, JIS K6301: < -65 °C Compression Set, JIS K6301: 55 % Coefficient of Linear Thermal Expansion, TMA: 16e-5 1/K |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields