Manufacturer: SABIC
Produced At: Import/ China
Product Category: Polycarbonate
Product No: CYCOLAC Resin FR15U
Product Quantity: 25KG / BAG
Product Features: Flame Retardant,Good Moldability,UV Resistant
CYCOLAC? Resin FR15U
Features |
|
Processing Method |
|
Multi-Point Data |
|
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | |||
-- | 1.19 | ASTM D792 | |
-- | 1.19 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) | |||
230°C/3.8 kg | 3.3 | g/10 min | ASTM D1238 |
220°C/5.0 kg | 7.0 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.44 | in3/10min | ISO 1133 |
Molding Shrinkage - Flow (0.126 in) | 5.0E-3 to 7.0E-3 | in/in | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 300000 | psi | ASTM D638 |
-- | 321000 | psi | ISO 527-2/1 |
Tensile Strength | |||
Yield 4 | 5500 | psi | ASTM D638 |
Yield | 5960 | psi | ISO 527-2/50 |
Break 4 | 4400 | psi | ASTM D638 |
Tensile Elongation | |||
Yield 4 | 2.4 | % | ASTM D638 |
Break 4 | 17 | % | ASTM D638 |
Break | 22 | % | ISO 527-2/50 |
Flexural Modulus | |||
1.97 in Span 5 | 340000 | psi | ASTM D790 |
-- 6 | 328000 | psi | ISO 178 |
Flexural Stress | |||
-- 6, 7 | 9180 | psi | ISO 178 |
Yield, 1.97 in Span 5 | 9800 | psi | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | |||
73°F | 4.0 | ft·lb/in | ASTM D256 |
73°F 8 | 5.7 | ft·lb/in2 | ISO 180/1A |
Instrumented Dart Impact (73°F, Total Energy) | 252 | in·lb | ASTM D3763 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
66 psi, Unannealed, 0.126 in | 187 | °F | |
264 psi, Unannealed, 0.126 in | 167 | °F | |
Vicat Softening Temperature | |||
-- | 201 | °F | ASTM D1525 9 |
-- | 198 | °F | ISO 306/B50 |
CLTE | ASTM E831 | ||
Flow : -40 to 104°F | 5.0E-5 | in/in/°F | |
Transverse : -40 to 104°F | 5.1E-5 | in/in/°F | |
RTI Elec | 194 | °F | UL 746 |
RTI Imp | 185 | °F | UL 746 |
RTI Str | 194 | °F | UL 746 |
Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength (0.126 in, in Oil) | 510 | V/mil | IEC 60243-1 |
Arc Resistance 10 | PLC 7 | ASTM D495 | |
Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
Hot-wire Ignition (HWI) | PLC 2 | UL 746 | |
Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
0.06 in | V-0 | ||
0.11 in | 5VA |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (392°F, 1000 sec^-1) | 320 | Pa·s | ASTM D3835 |
Injection | Nominal Value | Unit | |
Drying Temperature | 180 to 190 | °F | |
Drying Time | 2.0 to 4.0 | hr | |
Drying Time, Maximum | 8.0 | hr | |
Suggested Max Moisture | 0.10 | % | |
Suggested Shot Size | 50 to 70 | % | |
Rear Temperature | 340 to 360 | °F | |
Middle Temperature | 390 to 410 | °F | |
Front Temperature | 400 to 430 | °F | |
Nozzle Temperature | 400 to 450 | °F | |
Processing (Melt) Temp | 400 to 450 | °F | |
Mold Temperature | 120 to 160 | °F | |
Back Pressure | 50.0 to 100 | psi | |
Screw Speed | 30 to 60 | rpm | |
Vent Depth | 1.5E-3 to 2.0E-3 | in |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields