Manufacturer: Celanese(DUPONT)
Produced At: Import/ China
Product Category: NYLON 6/PA6
Product No: Zytel 73G30HSL BK416
Product Quantity: 25KG / BAG
Product Features: Heat Stabilized
Zytel? 73G30HSL BK416
Filler / Reinforcement |
|
Additive |
|
Features |
|
RoHS Compliance |
|
Processing Method |
|
Multi-Point Data |
|
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
|
Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.36 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.60 | -- | % | |
Flow | 0.20 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 73°F, 0.0787 in | 6.3 | -- | % | |
Equilibrium, 73°F, 0.0787 in, 50% RH | 1.9 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 1.45E+6 | 870000 | psi | ISO 527-2 |
Tensile Stress (Break) | 27600 | 17400 | psi | ISO 527-2 |
Tensile Strain (Break) | 3.5 | 6.0 | % | ISO 527-2 |
Flexural Modulus | 1.23E+6 | -- | psi | ISO 178 |
Flexural Stress | 36300 | -- | psi | ISO 178 |
Poisson's Ratio | 0.34 | 0.35 | ISO 527 | |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-40°F | 4.8 | -- | ft·lb/in2 | |
-22°F 3 | 4.8 | 10 | ft·lb/in2 | |
73°F | 7.6 | 11 | ft·lb/in2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-22°F | 38 | 38 | ft·lb/in2 | |
73°F | 48 | 48 | ft·lb/in2 | |
Notched Izod Impact Strength | ISO 180/1A | |||
-40°F | 5.2 | -- | ft·lb/in2 | |
73°F | 7.1 | 9.5 | ft·lb/in2 |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
66 psi, Unannealed | 428 | -- | °F | ISO 75-2/B |
264 psi, Unannealed | 399 | -- | °F | ISO 75-2/A |
Glass Transition Temperature 4 | 140 | -- | °F | ISO 11357-2 |
Melting Temperature 4 | 430 | -- | °F | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow | 6.7E-6 | -- | in/in/°F | |
Flow : -40 to 73°F | 1.4E-5 | -- | in/in/°F | |
Flow : 131 to 320°F | 6.7E-6 | -- | in/in/°F | |
Transverse | 5.6E-5 | -- | in/in/°F | |
Transverse : -40 to 73°F | 4.2E-5 | -- | in/in/°F | |
Transverse : 131 to 320°F | 7.2E-5 | -- | in/in/°F |
Flammability | Dry | Conditioned | Unit | Test Method |
Burning Rate 5 (0.0394 in) | 1.2 | -- | in/min | ISO 3795 |
Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
0.030 in | HB | -- | ||
0.06 in | HB | -- | ||
FMVSS Flammability | B | -- | FMVSS 302 | |
Fogging | ISO 6452 | |||
F-value (refraction) | 95 | -- | % | |
G-value (condensate) | 1.0E-4 | -- | g |
Additional Information | Dry | Conditioned | Unit | Test Method |
Emission of Organic Compounds | 8.50 | -- | μgC/g | VDA 277 |
Odor | 3.50 | -- | VDA 270 |
Injection | Dry | Unit | |
Drying Temperature | 176 | °F | |
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
Suggested Max Moisture | 0.20 | % | |
Processing (Melt) Temp | 500 to 536 | °F | |
Melt Temperature, Optimum | 518 | °F | |
Mold Temperature | 158 to 248 | °F | |
Mold Temperature, Optimum | 212 | °F | |
Holding Pressure | 7250 to 14500 | psi | |
Drying Recommended | yes | ||
Hold Pressure Time | 3.00 | s/mm | |
Maximum Screw Tangential Speed | 472 | in/min |
Products are widely used in plastic modification, automotive, construction, electrical and electronic, industrial, daily necessities and other fields