CYCOLOY? FR Resin CY6110
聚碳酸酯+丙烯腈丁二烯苯乙烯
產品說明:
CYCOLOY CY6110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a hydrolytically stable, impact modified grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CY6110 resin is an excellent candidate for a wide variety of large size of applications including appliances, lighting, electrical and enclosures.
添加劑 | |
特性 | - Chlorine Free、抗撞擊性，良好、良好的流動性、水解穩(wěn)定、無溴、阻燃性
|
用途 | - Lighting Applications、電氣/電子應用領域、電器用具、電子顯示器
|
加工方法 | |
Also Available In | |
密度 | 1.18 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (260°C/2.16 kg) | 1.40 | in3/10min | ISO 1133 |
收縮率 - 流動 (0.126 in) | 4.0E-3 到 6.0E-3 | in/in | 內部方法 |
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.60 | % |
|
平衡, 73°F, 50% RH | 0.20 | % |
|
拉伸模量 |
|
|
|
-- 3 | 400000 | psi | ASTM D638 |
-- | 399000 | psi | ISO 527-2/1 |
抗張強度 |
|
|
|
屈服 4 | 9140 | psi | ASTM D638 |
屈服 | 9140 | psi | ISO 527-2/50 |
斷裂 4 | 6820 | psi | ASTM D638 |
斷裂 | 6670 | psi | ISO 527-2/50 |
伸長率 |
|
|
|
屈服 4 | 4.1 | % | ASTM D638 |
屈服 | 4.0 | % | ISO 527-2/50 |
斷裂 4 | 65 | % | ASTM D638 |
斷裂 | 35 | % | ISO 527-2/50 |
彎曲模量 5 | 354000 | psi | ISO 178 |
彎曲應力 5, 6 | 13600 | psi | ISO 178 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-22°F 7 | 4.8 | ft·lb/in2 |
|
73°F 7 | 21 | ft·lb/in2 |
|
73°F 8 | 16 | ft·lb/in2 |
|
懸壁梁缺口沖擊強度 |
|
|
|
-22°F | 1.9 | ft·lb/in | ASTM D256 |
73°F | 8.9 | ft·lb/in | ASTM D256 |
-22°F 9 | 4.8 | ft·lb/in2 | ISO 180/1A |
-22°F 10 | 5.7 | ft·lb/in2 | ISO 180/1A |
73°F 9 | 21 | ft·lb/in2 | ISO 180/1A |
73°F 10 | 12 | ft·lb/in2 | ISO 180/1A |
熱變形溫度 10 |
|
|
|
66 psi, 未退火, 0.157 in, 2.52 in 跨距 | 208 | °F | ISO 75-2/Bf |
264 psi, 未退火, 0.157 in, 2.52 in 跨距 | 190 | °F | ISO 75-2/Af |
維卡軟化溫度 |
|
|
|
-- | 219 | °F | ISO 306/B50 |
-- | 223 | °F | ISO 306/B120 |
Ball Pressure Test (163 到 171°F) | 通過 |
| IEC 60695-10-2 |
線形熱膨脹系數 |
|
| ISO 11359-2 |
流動 : -40 到 104°F | 4.4 | in/in/°F |
|
橫向 : -40°F | 4.4 | in/in/°F |
|
RTI Elec | 185 | °F | UL 746 |
RTI Imp | 185 | °F | UL 746 |
RTI | 185 | °F | UL 746 |
表面電阻率 | 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 |
|
| IEC 60243-1 |
0.0315 in, 在油中 | 1200 | V/mil |
|
0.0630 in, 在油中 | 790 | V/mil |
|
相對電容率 |
|
| IEC 60250 |
50 Hz | 2.90 |
|
|
60 Hz | 2.90 |
|
|
1 MHz | 2.90 |
|
|
耗散因數 |
|
| IEC 60250 |
50 Hz | 2.0E-3 |
|
|
60 Hz | 2.0E-3 |
|
|
1 MHz | 7.0E-3 |
|
|
相比耐漏電起痕指數(CTI) | PLC 2 |
| UL 746 |
熱絲引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等級 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.10 in | 5VB |
|
|
灼熱絲易燃指數 (0.04 in) | 1760 | °F | IEC 60695-2-12 |
熱燈絲點火溫度 |
|
| IEC 60695-2-13 |
0.04 in | 1520 | °F |
|
0.08 in | 1520 | °F |
|
0.12 in | 1520 | °F |
|
極限氧指數 | 31 | % | ISO 4589-2 |
干燥溫度 | 176 到 194 | °F |
|
干燥時間 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
料斗溫度 | 140 到 176 | °F |
|
料筒后部溫度 | 446 到 536 | °F |
|
料筒中部溫度 | 464 到 554 | °F |
|
料筒前部溫度 | 482 到 572 | °F |
|
射嘴溫度 | 482 到 572 | °F |
|
加工（熔體）溫度 | 482 到 572 | °F |
|
模具溫度 | 140 到 185 | °F |
|
排氣孔深度 | 1.2E-3 到 3.0E-3 | in |
|