ForTii? F81
Polyamide 4T
產(chǎn)品說明:
15% Glass Reinforced, Improved flow, Flame Retardant, Halogen free and free of red phosphorous
Special Features:
ForTii? is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii? in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.34 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.2 | -- | % |
|
流量 | 0.50 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 5.8 | -- | % |
|
平衡, 73°F, 50% RH | 2.2 | -- | % |
|
拉伸模量 | 1.02E+6 | 1.02E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 15200 | 16000 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 2.0 | 2.1 | % | ISO 527-2 |
彎曲模量 | 1.02E+6 | 1.02E+6 | psi | ISO 178 |
彎曲應(yīng)力 | 26100 | 25400 | psi | ISO 178 |
簡支梁缺口沖擊強(qiáng)度 (73°F) | 3.3 | 3.3 | ft·lb/in2 | ISO 179/1eA |
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 14 | 14 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 608 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 572 | -- | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 3 | 257 | -- | °F | ISO 11357-2 |
熔融溫度 3 | 617 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ASTM D696 |
流動 | 2.2E-5 | -- | in/in/°F |
|
橫向 | 3.1E-5 | -- | in/in/°F |
|
介電強(qiáng)度 | 840 | -- | V/mil | IEC 60243-1 |
漏電起痕指數(shù) | 600 | -- | V | IEC 60112 |
可燃性等級 (0.030 in) | V-0 | -- |
| IEC 60695-11-10, -20 |
干燥溫度 | 212 | °F |
|
干燥時(shí)間 | 4.0 到 8.0 | hr |
|
料筒后部溫度 | 608 到 626 | °F |
|
料筒中部溫度 | 617 到 635 | °F |
|
料筒前部溫度 | 626 到 635 | °F |
|
射嘴溫度 | 626 到 635 | °F |
|
加工（熔體）溫度 | 626 到 644 | °F |
|
模具溫度 | 212 到 302 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 72.5 到 435 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！