Ultrason? E 3010
聚醚砜
產品說明:
Ultrason E 3010 is an unfilled, higher viscosity injection molding and extrusion PESU grade, tougher and with improved chemical resistance.
特性 | |
機構評級 | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點數據 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 | 1.37 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (360°C/10.0 kg) | 2.14 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.90 | % |
|
流量 | 0.85 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 2.2 | % |
|
平衡, 73°F, 50% RH | 0.80 | % |
|
球壓硬度 | 22300 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 384000 | psi | ISO 527-2 |
拉伸應力 (屈服, 73°F) | 12300 | psi | ISO 527-2 |
拉伸應變 (屈服, 73°F) | 6.9 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
| ISO 179 |
-22°F | 3.8 | ft·lb/in2 |
|
73°F | 3.8 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179 |
-22°F | 無斷裂 |
|
|
73°F | 無斷裂 |
|
|
懸壁梁缺口沖擊強度 |
|
| ISO 180 |
-22°F | 3.8 | ft·lb/in2 |
|
73°F | 3.8 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 405 | °F | ISO 75-2/A |
線形熱膨脹系數 - 流動 | 2.9E-5 | in/in/°F |
|
RTI Elec |
|
| UL 746 |
0.06 in | 356 | °F |
|
0.12 in | 356 | °F |
|
RTI Imp |
|
| UL 746 |
0.06 in | 356 | °F |
|
0.12 in | 356 | °F |
|
RTI |
|
| UL 746 |
0.06 in | 374 | °F |
|
0.12 in | 374 | °F |
|
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 860 | V/mil | IEC 60243-1 |
介電常數 |
|
| IEC 60250 |
100 Hz | 3.90 |
|
|
1 MHz | 3.80 |
|
|
耗散因數 |
|
| IEC 60250 |
100 Hz | 1.7E-3 |
|
|
1 MHz | 0.014 |
|
|
漏電起痕指數 | 125 | V | IEC 60112 |
UL 阻燃等級 |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.12 in | V-0 |
|
|
干燥溫度 | 266 到 302 | °F |
|
干燥時間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 644 到 734 | °F |
|
模具溫度 | 284 到 356 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|