Ixef? FC-1022

Ixef? FC-1022

產(chǎn)品產(chǎn)商：索爾維（SOLVAY）
產(chǎn)品產(chǎn)地：進口/中國
產(chǎn)品類別：IXEF PARA
產(chǎn)品型號：Ixef FC-1022
產(chǎn)品規(guī)格：25KG/包
產(chǎn)品特性：超強剛性，尺寸穩(wěn)定性良好，出色的外觀，低吸濕性，高強度，好的消毒性，良好的抗蠕變性，流動性高，耐化學(xué)性良好，食品接觸，合規(guī)性，通用

Ixef? FC-1022

聚丙烯酰胺
產(chǎn)品說明:
Ixef? FC-1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Ixef? FC-1022 is approved for food contact and meets FDA regulations for Ixef? FC-1022 NT 000 (natural) and Ixef? FC-1022 BK 001 (black) based on clearances granted by FCN 001242 for repeated use food contact applications with all food types, under FDA conditions of use B through H as described in Tables 1 and 2 of 21 CFR 176.170(c).

  • Black: FC-1022 BK 001

  • Natural: FC-1022 NT 000

填料/增強材料

  • 玻璃纖維增強材料, 50% 填料按重量

特性
  • 超強剛性,尺寸穩(wěn)定性良好,出色的外觀,低吸濕性,高強度,好的消毒性,良好的抗蠕變性,流動性高,耐化學(xué)性良好,食品接觸的合規(guī)性,通用
用途
  • 電器用具,高光應(yīng)用,食品服務(wù)領(lǐng)域,醫(yī)療器材
機構(gòu)評級
  • FDA 21 CFR 176.170(c) 3NSF 51 4歐洲 10/1/2011 12:00:00 AM
RoHS 合規(guī)性

  • RoHS 合規(guī)

外觀
  • 黑色,自然色
形式

  • 粒子

加工方法

  • 注射成型

物理性能
干燥
調(diào)節(jié)后的
單位制
測試方法
密度
1.64
--
g/cm3
ISO 1183
收縮率
0.10 到 0.30
--
%
ISO 294-4
吸水率 (73°F, 24 hr)
0.16
--
%
ISO 62
機械性能
干燥
調(diào)節(jié)后的
單位制
測試方法
拉伸模量
2.83E+6
2.83E+6
psi
ISO 527-2
拉伸應(yīng)力 (斷裂)
40600
37700
psi
ISO 527-2
拉伸應(yīng)變 (斷裂)
1.9
2.2
%
ISO 527-2
彎曲模量
2.68E+6
--
psi
ISO 178
彎曲應(yīng)力
55100
--
psi
ISO 178
沖擊性能
干燥
調(diào)節(jié)后的
單位制
測試方法
懸壁梁缺口沖擊強度
2.1
--
ft·lb/in
ASTM D256
無缺口懸臂梁沖擊
16
--
ft·lb/in
ASTM D256
熱性能
干燥
調(diào)節(jié)后的
單位制
測試方法
熱變形溫度 (264 psi, 未退火)
446
--
°F
ISO 75-2/A
線形熱膨脹系數(shù) - 流動
8.3E-6
--
in/in/°F
ISO 11359-2
補充信息
干燥
調(diào)節(jié)后的


吸水性 - Equil, 65% RH
--



注射
干燥
單位制

干燥溫度
248
°F

干燥時間
0.50 到 1.5
hr

料筒后部溫度
482 到 500
°F

料筒前部溫度
500 到 554
°F

射嘴溫度
500 到 554
°F

加工（熔體）溫度
536
°F

模具溫度
248 到 284
°F

注射速度
快速


注射說明
Hot runners: 250°C to 260°C (482°C to 500°F)

Storage
Ixef? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef? processing guide.

Drying
The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F).

Injection Molding
Ixef? FC-1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure.

The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F).

To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).


如需索爾維（SOLVAY）原廠物性表及相關(guān)文件，請聯(lián)系我們工作人員，謝謝！